Super high temperature insulation
Siliglass
Siligalss is high silicate heat resistant fiberglass consisted of SiO2 by 96% or more and can be used for long hours under high temperature of 1,000°C or higher. It is excellent in thermal durability, chemical stability and electrical insulation properties.
Characteristics
- Asbestos Free
- Fireproof
- Resists Thermal Shock
- Resists Chemicals
- Electrical Resistivity
- Minimal Shrinkage
- Resists Molten Steel
- Non-Hazardous
- Cost Effective
- Good Workability
Applications
-
High temperature thermal insulation and absorption material
Welding & Burning Protection Drop Cloth, Welding Curtains, Furnace Curtain, Heat Treat & Stress Relief Insulation -
High temperature filter media
Filter media for hot gases and chemicals. -
High temperature structural materials
Rocket nose cones, etc. - Wicks of oil heater
-
Catalytic carrier for oxidation-reduction reaction
Catalytic carrier of deodorization equipment. Treating material for organic solution gas. -
Others
Electric cable insulator for hair driers. High temperature buffers and seals.
Cloth
![[photo]Cloth](img/heat01.jpg)
![[photo]Cloth](img/heat02.jpg)
![[photo]Cloth](img/heat03.jpg)
Standard specification
| Product Code | Thickness (mm) |
Width (mm) |
Length (m) |
Weight (g/m2) |
Product Tensile Strength (N/25mm) |
Tensile Strength After Heating (N/25mm) |
Heat Shrinkage (%) |
Weave | ||
|---|---|---|---|---|---|---|---|---|---|---|
| Warp | Weft | Warp | Weft | |||||||
| BCM-430 | 0.40 | 525 | 100 | 270 | >78 | >78 | >29 | >29 | <5.0 | Mock Lemo |
| BCA-650 | 0.60 | 1,000 | 50 | 460 | >196 | >127 | >137 | >88 | <7.0 | Twill |
| BCS-665 | 0.62 | 1,000 | 87 | 630 | >294 | >137 | >196 | >98 | <4.5 | Satin |
| BCS-665AD | 0.65 | 1,000 | 50 | 570 | >490 | >294 | >196 | >98 | <7.0 | Satin |
| BCS-665U | 0.60 | 1,000 | 50 | 570 | >343 | >196 | >196 | >98 | <15.0 | Satin |
| BCS-12 | 1.20 | 1,000 | 50 | 1,190 | >392 | >245 | >343 | >196 | <7.0 | Satin |
| BCS-12U | 1.20 | 1,000 | 50 | 1,070 | >735 | >490 | >343 | >196 | <15.0 | Satin |
| BCS-12AD | 1.25 | 1,000 | 500 | 1,190 | >882 | >637 | >343 | >196 | <7.0 | Satin |
- Heat shrinkage : Percentage of length reduction with 1100°C applied for 30 minutes. (BCS-665 is with 1200°C applied for 30 minutes)
- Tensile strength after heating : Retension of tensile strength after 30 minutes heating at 1100°C. (BCS-665 is after 30 minutes heating at 1200°C)
- BCS-665U,BCS-665AD,BCS-12U and BCS-12 are JIS A 1323(flame resisting examination)passing goods.
Tape, Sleeving, Rope, Yarn
![[photo]Tape, Sleeving, Rope, Yarn](img/heat04.jpg)
Standard specification
| Product Code | Thickness (mm) |
Width (mm) |
Length (m) |
Product Tensile Strength (N/25mm) |
Tensile Strength After Heating (N/25mm) |
Heat Shrinkage (%) |
Weave |
|---|---|---|---|---|---|---|---|
| BTH-225 | 0.20 | 25 | 80 | >78 | >59 | <7.0 | Plain |
| BTA-425 | 0.35 | 25 | 50 | >137 | >98 | <7.0 | Twill |
| BTA-450 | 0.35 | 50 | 50 | >137 | >98 | <7.0 | Twill |
| BTA-625 | 0.60 | 25 | 50 | >196 | >137 | <7.0 | Twill |
| BTA-650 | 0.60 | 50 | 50 | >196 | >137 | <7.0 | Twill |
| BTN-1550U | 1.50 | 50 | 50 | >196/width | >137/width | <15.0 | Warp Backed |
| Product Code | Standard Inner Diameter (mmφ) |
Pitch (Per 25mm) |
Length (m) |
Heat Shrinkage (%) |
|---|---|---|---|---|
| BS-1 | 1 | 18 | 30 | <7.0 |
| BS-2 | 2 | 17 | 30 | <7.0 |
| BS-3 | 3 | 15 | 30 | <7.0 |
| BS-5 | 5 | 15 | 30 | <7.0 |
| BS-8 | 8 | 17 | 30 | <7.0 |
| BS-20 | 20 | 13 | 30 | <7.0 |
| Product Code | Standard Inner Diameter (mmφ) |
Standard Length (m) |
Heat Shrinkage (%) |
Braid |
|---|---|---|---|---|
| BRA-25U | 25 | 20 | <15 | Entwinement |
| Product Code | Count (g/km) |
Product Tensile Strength (N/yarn) |
Tensile Strength After Heating (N/yarn) |
Heat Shrinkage (%) |
|---|---|---|---|---|
| BY-850 | 850 | >78 | >19.6 | <7.0 |
- Heat shrinkage : Percentage of length reduction with 1100°C applied for 30 minutes.
- Tensil strength after heating : Retension of tensile strength after 30 minutes hearting at 1100°C.
This catalog is subject to change without any notice.